Show simple item record

dc.contributor.authorUğur, Şaziyetr_TR
dc.contributor.authorAlemdar, Ayşetr_TR
dc.contributor.authorPekcan, Mehmet Öndertr_TR
dc.date.accessioned2015-01-15T23:00:20Z
dc.date.available2015-01-15T23:00:20Z
dc.date.issued2005-07
dc.identifier.citationUgur, S., Alemdar, A., & Pekcan, Ö. (2005). Films formed from polystyrene latex/clay composites: A fluorescence study. JCT Research, 2(7), 565-575. doi:10.1007/s11998-005-0016-8en_US
dc.identifier.issn1547-0091
dc.identifier.otherWOS:000230804400008
dc.identifier.urihttp://hdl.handle.net/11729/176
dc.identifier.urihttp://dx.doi.org/10.1007/s11998-005-0016-8
dc.description.abstractThis study reports a steady-state fluorescence (SSF) technique for studying film formation from surractant-free polystyrene (PS) latex and Na-montmorillonite (SNaM) composites. The composite films were prepared from pyrene (P)-labeled PS particles and SNaM clay at room temperature and annealed at elevated temperatures in 10-min intervals above glass transition temperature (T-g) of polystyrene. During the annealing processes, the transparency of the fllm improved considerably. Scattered light (I-s) and fluorescence intensity (I-s) from P were measured after each annealing step to monitor the stages of film formation. Evolution of transparency of composite films was monitored by using photon transmission intensity, I-tr Scanning electron microscopy (SEM) was used to detect the variation in physical structure of annealed composite-films. Minimum flIm formation temperature, T-o, and healing temperatures, T-h, were determined. Void closure and interdiff-usion stages were modeled and related activation energies were determined. It was observed that both activation energies increased as the percent of SNaM was increased in composite films.en_US
dc.language.isoenen_US
dc.publisherFederation soc coatings technologyen_US
dc.relation.isformatof10.1007/s11998-005-0016-8
dc.rightsinfo:eu-repo/semantics/closedAccessen_US
dc.sourceJournal of Coatings Technology Researchen_US
dc.subjectLayered silicate nanocompositesen_US
dc.subjectPolymer-polymer interfaceen_US
dc.subjectPoly(methyl methacrylate)en_US
dc.subjectPhoton transmissionen_US
dc.subjectEnergy-transferen_US
dc.subjectParticlesen_US
dc.subjectDiffusionen_US
dc.subjectDensityen_US
dc.subjectInterdiffusionen_US
dc.subjectViscosityen_US
dc.titleFilms formed from polystyrene latex/clay composites: A fluorescence studyen_US
dc.typearticleen_US
dc.description.versionPublisher's Versionen_US
dc.contributor.departmentIşık Üniversitesi, Fen Edebiyat Fakültesi, Fizik Bölümütr_TR
dc.contributor.departmentIsik University, Faculty of Arts and Sciences, Department of Physicsen_US
dc.contributor.authorIDTR151504
dc.contributor.authorIDTR9155
dc.identifier.volume2
dc.identifier.issue7
dc.identifier.startpage565
dc.identifier.endpage575
dc.peerreviewedYesen_US
dc.publicationstatusPublisheden_US


Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record