Poly (styrene) latex/modified na-activated bentonite nanocomposite films: a fluorescence study
Künye
Uğur, Ş., Yargı, Ö., Günister, E. & Pekcan, M. Ö. (2008). Poly (styrene) latex/modified na-activated bentonite nanocomposite films: A fluorescence study. Applied Clay Science, 42(1-2), 39-49. doi:10.1016/j.clay.2008.02.009Özet
We studied film formation of composites of surfactant-free polystyrene (PS) nanoparticles and modified Na-activated bentonite (MLB), by steady state fluorescence (SSF) technique. The films were prepared from a mixture of pyrene (P)-labeled PS particles and MLB at various compositions at room temperature. These films were annealed at elevated temperatures above the glass transition (T(g)) temperature of polystyrene for 10 min. Scattered light (I(S)) and fluorescence intensities (I(P)) from P were measured after each annealing step to monitor the stages of film formation. Evolution of transparency of the composite films was monitored by using photon transmission intensity, I(tr) Atomic force microscopy (AFM) was used to detect the variation in physical structure of annealed composite films. The nanocomposite films exhibited a percolation threshold at 20 wt.% MLB content. Below this fraction two distinct film formation stages were observed which are known as void closure and interdiffusion and above this fraction no film formation was detected. At 0-20 wt.% MLB, minimum film formation, T(0), void closure, T(v) and healing, T(h) temperatures were determined. Void closure and interdiffusion stages were modeled and related activation energies were determined. Void closure activation energies decreased as the percent of MLB increased, no variation was observed in backbone activation energies.
Cilt
42Sayı
1-2Koleksiyonlar
İlgili Öğeler
Başlık, yazar, küratör ve konuya göre gösterilen ilgili öğeler.
-
Temperature effect on drying and swelling of kappa carrageenan gels: A steady state fluorescence study
Tarı İlgin, Özlem; Pekcan, Mehmet Önder (Wiley-V C H Verlag GMBH, 2008)A novel technique based on in situ steady state fluorescence (SSF) measurements is introduced for studying drying and swelling Of kappa(-) carrageenan (kappa carrageenan) gels at various temperatures. kappa(-) carrageenan ... -
Drying of PAAm hydrogels at various temperatures: A fluorescence study
Aktaş, Demet Kaya; Evingür, Gülşen Akın; Pekcan, Mehmet Önder (Taylor & Francis Group, 2007-05)The steady-state fluorescence (SSF) technique was employed for studying the drying of polyacrylamide (PAAm) hydrogels. Disc-shaped hydrogels were prepared by free-radical crosslinking copolymerization of acrylamide (AAm) ... -
In situ fluorescence study of swelling, sorption and desorption processes in and out of PAAm gels
Evingür, Gülşen Akın; Karslı, Kadir; Pekcan, Mehmet Önder (Wiley-V C H Verlag GMBH, 2008-05)Small molecule sorption and desorption in and out of polyacrylamide (PAAm) gels were studied at various temperatures. Pyranine (P(y)) dissolved in water used as a probe. Fluorescence emission intensity, I(p) from P(y) was ...