8 sonuçlar
Arama Sonuçları
Listeleniyor 1 - 8 / 8
Yayın Film formation from TiO2-polystyrene latex composite: a fluorescence study(Taylor & Francis Group, 2007-03-01) Uğur, Şaziye; Sunay Yapışkan, Münüre Selin; Tepehan, Fatma Zehra; Pekcan, Mehmet ÖnderThis work reports the use of the steady state fluorescence (SSF) technique for studying film formation from TiO2 covered polystyrene (PS) latex particles. The composite films were prepared from pyrene (P)-labeled PS particles by covering them with TiO2 at room temperature and then annealed at elevated temperatures in 10 min time interval above glass transition (T-g) temperature of polystyrene. Five different composite films were studied in various TiO2 layer contents. Fluorescence intensities Ip from P were measured after each annealing step to monitor the stages of film formation. Films showed considerable increase in Ip above the certain onset temperature called minimum film forming temperature, T-0. Void closure and interdiffusion stages were modeled and related activation energies were determined and found to be 23.12 and 92.80 kJ mol(-1), respectively.Yayın Poly (styrene) latex/modified na-activated bentonite nanocomposite films: a fluorescence study(Elsevier Science BV, 2008-12) Uğur, Şaziye; Yargı, Önder; Günister, Ebru; Pekcan, Mehmet ÖnderWe studied film formation of composites of surfactant-free polystyrene (PS) nanoparticles and modified Na-activated bentonite (MLB), by steady state fluorescence (SSF) technique. The films were prepared from a mixture of pyrene (P)-labeled PS particles and MLB at various compositions at room temperature. These films were annealed at elevated temperatures above the glass transition (T(g)) temperature of polystyrene for 10 min. Scattered light (I(S)) and fluorescence intensities (I(P)) from P were measured after each annealing step to monitor the stages of film formation. Evolution of transparency of the composite films was monitored by using photon transmission intensity, I(tr) Atomic force microscopy (AFM) was used to detect the variation in physical structure of annealed composite films. The nanocomposite films exhibited a percolation threshold at 20 wt.% MLB content. Below this fraction two distinct film formation stages were observed which are known as void closure and interdiffusion and above this fraction no film formation was detected. At 0-20 wt.% MLB, minimum film formation, T(0), void closure, T(v) and healing, T(h) temperatures were determined. Void closure and interdiffusion stages were modeled and related activation energies were determined. Void closure activation energies decreased as the percent of MLB increased, no variation was observed in backbone activation energies.Yayın Films formed from polystyrene latex/clay composites: A fluorescence study(Springer New York, 2005-07) Uğur, Şaziye; Alemdar, Ayşe; Pekcan, Mehmet ÖnderThis study reports a steady-state fluorescence (SSF) technique for studying film formation from surractant-free polystyrene (PS) latex and Na-montmorillonite (SNaM) composites. The composite films were prepared from pyrene (P)-labeled PS particles and SNaM clay at room temperature and annealed at elevated temperatures in 10-min intervals above glass transition temperature (T-g) of polystyrene. During the annealing processes, the transparency of the fllm improved considerably. Scattered light (I-s) and fluorescence intensity (I-s) from P were measured after each annealing step to monitor the stages of film formation. Evolution of transparency of composite films was monitored by using photon transmission intensity, I-tr Scanning electron microscopy (SEM) was used to detect the variation in physical structure of annealed composite-films. Minimum flIm formation temperature, T-o, and healing temperatures, T-h, were determined. Void closure and interdiff-usion stages were modeled and related activation energies were determined. It was observed that both activation energies increased as the percent of SNaM was increased in composite films.Yayın Film formation from nano-sized polystrene latex covered with various TiO2 layers(Wiley, 2006-12) Uğur, Şaziye; Sunay, Selin; Elaissari, Abdelhamid; Tepehan, Fatma Zehra; Pekcan, Mehmet ÖnderSteady-state fluorescence technique was used for studying film formation from TiO2 covered nano-sized polystyrene latex particles. The composite films were prepared from pyrene (P)-labeled PS particles by covering them with various layers of TiO2 at room temperature. These films then annealed at elevated temperatures in 10 min time interval above glass transition (T-g) temperature of polystyrene. Five different composite films were studied in various TiO2 layer contents. Fluorescence emission intensity, I-P from P was measured after each annealing step to monitor the stages of film formation. Films present significant increase in I-P above the certain onset temperature called minimum film forming temperature, To. However, at higher annealing temperatures, I-P showed a decrease. Increase and decrease in I-P were modeled by void closure and interdiffusion processes and related activation energies were determined, respectively. Dissolution of annealed PS film, with high TiO2 content presented a nice, ordered nanosized ceramic structure, which may predict the construction of nano-layer photonic crystals.Yayın Film formation from nano-sized polystyrene latex particles(John Wiley & Sons Ltd, 2005-05) Uğur, Şaziye; Elaissari, Abdelhamid; Pekcan, Mehmet ÖnderThis work reports on the steady state fluorescence (SSF) technique for studying film formation from surfactant-free, nano-sized polystyrene (PS) latex particles prepared via emulsion polymerization. The latex films were prepared from pyrene M-labeled PS particles at room temperature and annealed at elevated temperatures in 5, 10, 15, 20 and 30 min time intervals above the glass transition temperature (T-g) of PS. During the annealing processes, the transparency of the film was improved considerably. Monomer and excimer fluorescence intensities, I-p and I-E respectively, from P were measured after each annealing step to monitor the stages of film formation. Evolution of transparency of the latex films was monitored by using photon transmission intensity, It,. Void closure and interdiffusion stages were modeled and related activation energies were determined and found to be 10.3 and 50.3 kJ mol(-1). Void closure temperatures, T-v, were determined from the minima of I-tr value. CopyrightYayın Film formation from PS latex doped PNIPAM hydrogels at various heating and cooling rates(VSP BV, Brill Academic Publishers, 2008-05-01) Uğur, Şaziye; Yargı, Önder; Pekcan, Mehmet ÖnderFilm formation from polystrene (PS) latex doped poly(N-isopropylacrylamide) (PNIPAM) hydrogels was studied by using photon transmission technique. The transmitted light intensity, It, was monitored during film formation process. Films were prepared by annealing, 10 wt% PS doped PNIPAM particles at five different heating and cooling rates at temperatures ranging from 10 to 100 degrees C. I-tr presented a hysteresis loops during heating-cooling cycles, which were explained by void closure and void reconstruction processes. The corresponding activation energies were measured during reversible film formation process. Void closure and void reconstruction models were introduced to produce the activation energies.Yayın Film formation from pure and mixed latices; transient fluorescence study(Academic Press Inc Elsevier Science, 2005-11-15) Uğur, Şaziye; Pekcan, Mehmet ÖnderA fast transient fluorescence technique was used to study latex film formation induced by organic solvent vapor. Mixtures of pyrene (P)- and naphthalene (N)-labeled and/or pure naphthalene-labeled latex films were prepared separately from poly(methyl methacrylate) (PMMA) particles. Then these pure and mixed latex films were exposed to vapor of various chloroform-heptane mixtures in seven different experiments. In both films, fluorescence lifetimes from N were monitored during vapor-induced film formation. It was observed that N lifetimes decreased as the vapor exposure time is increased. A Stern-Volmer kinetic analysis was used for low quenching efficiencies to interpret the decrease in N lifetimes. A Prager-Tirrell model was employed to obtain back-and-forth frequencies, v, of reptating PMMA chains during latex film formation induced by solvent vapor. In both pure and mixed latex films, v values were found to be correlated with the chloroform content in the vapor mixture. It was observed that polymer interdiffusion obeyed a t(1/2) law during film formation.Yayın Ceramic encapsulated latex composites(Elsevier Inc, 2006-04-15) Uğur, Şaziye; Pehlivan, Esat; Tepehan, Fatma Zehra; Pekcan, Mehmet ÖnderThis work reports the encapsulation of latex particles in Al(2)O(3)-polystyrene (PS) composite films. These films were prepared from PS particles in Al(2)O(3) dispersion at room temperature in various latex contents. Composite films were annealed at elevated temperatures in 10 min time interval above the glass transition temperature (T,,) of polystyrene. Transmitted photon intensities. I(tr) were monitored after each annealing step. AFM micrographs were also used to observe the physical changes of the composite films during annealing. It was observed that latex particles are encapsulated above a critical Al(2)O(3) content of 33 wt% which corresponds to the critical occupation probability of p(c) = 0.33 at which the film obey the site-percolation model with a critical exponent of 0.45. Below pc it was seen that complete latex film formation process took place, where transparency of the film was increased by annealing.
