3 sonuçlar
Arama Sonuçları
Listeleniyor 1 - 3 / 3
Yayın Vapor-induced film formation from low-T-g particles for different solvent compositions(Elsevier Inc, 2006-05-15) Arda, Ertan; Kara, Selim; Saraç, Ayfer; Pekcan, Mehmet ÖnderThe photon transmission method was used to study latex film formation from poly(vinyl acetate) (PVAc) particles induced by two different solvents. Films with the same latex content were prepared from PVAc particles and exposed to vapor of ethanol-water and acetone-water mixtures in various compositions. Transmitted photon intensities, I-tr, from these films increased with increasing vapor exposure time. The increase in I-tr is attributed to the increase in crossing density at the polymer-polymer junction. The Prager-Tirrell model was employed to obtain the back-and-forth frequency, v, of the reptating polymer chain during film formation induced by solvent vapor. It was observed that the produced v values increase as the solvent content is increased for both solvents. Abilities of both solvents to form films were interpreted with the solubility parameters of the solvents and the PVAc.Yayın Reversible film formation from PS doped PNIPAM particles in various compositions(John Wiley & Sons Inc, 2008-02) Uğur, Şaziye; Yargı, Önder; Pekcan, Mehmet ÖnderFilm formation from polystyrene (PS) doped poly(N-isopropylacrylamide) (PNIPAM) particles was studied using photon transmission technique. The transmitted light intensity, Itr, was monitored during film formation process. Films were prepared by mixing PS and PNIPAM particles in various compositions ranging from 5 to 50 %. Samples were separately heated and cooled in constant rate at temperatures ranging from 10 to 100 C. The increase and decrease in Itr during heating-cooling cycles were explained by void closure and void reconstruction processes. The corresponding activation energies were measured during the reversible film formation process. Percolation model was used to interpret the distribution of PS particles in PNIPAM lattice.Yayın Film formation from nano-sized polystrene latex covered with various TiO2 layers(Wiley, 2006-12) Uğur, Şaziye; Sunay, Selin; Elaissari, Abdelhamid; Tepehan, Fatma Zehra; Pekcan, Mehmet ÖnderSteady-state fluorescence technique was used for studying film formation from TiO2 covered nano-sized polystyrene latex particles. The composite films were prepared from pyrene (P)-labeled PS particles by covering them with various layers of TiO2 at room temperature. These films then annealed at elevated temperatures in 10 min time interval above glass transition (T-g) temperature of polystyrene. Five different composite films were studied in various TiO2 layer contents. Fluorescence emission intensity, I-P from P was measured after each annealing step to monitor the stages of film formation. Films present significant increase in I-P above the certain onset temperature called minimum film forming temperature, To. However, at higher annealing temperatures, I-P showed a decrease. Increase and decrease in I-P were modeled by void closure and interdiffusion processes and related activation energies were determined, respectively. Dissolution of annealed PS film, with high TiO2 content presented a nice, ordered nanosized ceramic structure, which may predict the construction of nano-layer photonic crystals.
